太赫兹晶体
新势力光电供应太赫兹晶体,具有品质高、非线性光学特*、光电系数大的特点。该系列太赫兹晶体应用广泛,包括:太赫兹发生器、太赫兹探测器、快速光电调制、光参量发生器、1.55μm倍频。
Physical Properties
DAST Crystal
Melting temperature
256℃
Refractive indices@720nm
n1=2.519, n2=1.720, n3=1.635
Nonlinear optical coefficients
d11(1318nm)=1010pm/V
d11(1542nm)=290pm/V, d26(1542nm)=39pm/V
Electro optic coefficients
r11(720nm)=92pm/V
r11(1313nm)=53pm/V
r11(1535nm)=47pm/V
Dielectric constants@3KHz
ε1=5.2, ε2=4.1, ε3=3.0
Phase matching for THz Generation
1300-1600nm
Physical Properties
OH1 Crystal
Melting temperature
212℃
Refractive indices@1319nm
n2=1.58, n3=2.15
Nonlinear optical coefficients@1900nm
d333=120±10pm/V
d223=13±2pm/V
d322=8.5±2pm/V
Electro optic coefficients
r333(633nm)=109±4pm/V
r333(785nm)=75±7pm/V
r333(1064nm)=56±2pm/V
r333(1319nm)=52±7pm/V
Phase matching for THz Generation
1200-1460nm
Physical Properties
DSTMS Crystal
Melting temperature
250℃
Refractive indices@1550nm
n1=2.07, n2=1.64
Nonlinear Optical Coefficients@1900nm
d111=214±20pm/V
d122=31±4pm/V
d212=35±4pm/V
Electro optic coefficients@1900nm
r111=37±3pm/V
Phase matching for THz Generation
1300-1700nm
Photorefractive Crystal KNbO3
Wavelength[nm]
Recording Time(t*ical)[s]
KNbO3:Fe
488
1
KNbO3:Mn
515
1
860
3
KNbO3:Fe reduced
488
0.01
515
0.01
KNbO3:Rh reduced
860
0.5
1064
50
www.NewOpto.com
-
新势力光电供应太赫兹晶体,具有品质高、非线性光学特*、光电系数大的特点。该系列太赫兹晶体应用广泛,包括:太赫兹发生器、太赫兹探测器、快速光电调制、光参量发生器、1.55μm倍频。
Physical Properties
|
DAST Crystal
|
Melting temperature
|
256℃
|
Refractive indices@720nm
|
n1=2.519, n2=1.720, n3=1.635
|
Nonlinear optical coefficients
|
d11(1318nm)=1010pm/V
|
d11(1542nm)=290pm/V, d26(1542nm)=39pm/V
|
|
Electro optic coefficients
|
r11(720nm)=92pm/V
|
r11(1313nm)=53pm/V
|
|
r11(1535nm)=47pm/V
|
|
Dielectric constants@3KHz
|
ε1=5.2, ε2=4.1, ε3=3.0
|
Phase matching for THz Generation
|
1300-1600nm
|
Physical Properties
|
OH1 Crystal
|
Melting temperature
|
212℃
|
Refractive indices@1319nm
|
n2=1.58, n3=2.15
|
Nonlinear optical coefficients@1900nm
|
d333=120±10pm/V
|
d223=13±2pm/V
|
|
d322=8.5±2pm/V
|
|
Electro optic coefficients
|
r333(633nm)=109±4pm/V
|
r333(785nm)=75±7pm/V
|
|
r333(1064nm)=56±2pm/V
|
|
r333(1319nm)=52±7pm/V
|
|
Phase matching for THz Generation
|
1200-1460nm
|
Physical Properties
|
DSTMS Crystal
|
Melting temperature
|
250℃
|
Refractive indices@1550nm
|
n1=2.07, n2=1.64
|
Nonlinear Optical Coefficients@1900nm
|
d111=214±20pm/V
|
d122=31±4pm/V
|
|
d212=35±4pm/V
|
|
Electro optic coefficients@1900nm
|
r111=37±3pm/V
|
Phase matching for THz Generation
|
1300-1700nm
|
Photorefractive Crystal KNbO3
|
Wavelength[nm]
|
Recording Time(t*ical)[s]
|
KNbO3:Fe
|
488
|
1
|
KNbO3:Mn
|
515
|
1
|
860
|
3
|
|
KNbO3:Fe reduced
|
488
|
0.01
|
515
|
0.01
|
|
KNbO3:Rh reduced
|
860
|
0.5
|
1064
|
50
|
www.NewOpto.com